Please use this identifier to cite or link to this item: http://idr.nitk.ac.in/jspui/handle/123456789/16310
Full metadata record
DC FieldValueLanguage
dc.contributor.authorReddy M.
dc.contributor.authorPrasad C.D.
dc.contributor.authorPatil P.
dc.contributor.authorRamesh M.R.
dc.contributor.authorRao N.
dc.date.accessioned2021-05-05T10:30:10Z-
dc.date.available2021-05-05T10:30:10Z-
dc.date.issued2021
dc.identifier.citationSurfaces and Interfaces Vol. 22 , , p. -en_US
dc.identifier.urihttps://doi.org/10.1016/j.surfin.2020.100810
dc.identifier.urihttp://idr.nitk.ac.in/jspui/handle/123456789/16310-
dc.description.abstractThe objective of the Present research work is to evaluate the hot corrosion resistance of plasma-sprayed 70% NiCrAlY+ 30% TiO2 and 70% NiCrAlY+ 25% Cr2O3+5% YSZ coatings on MDN 420 alloy. Hot corrosion tests are carried out under molten salt environment of Na2SO4+60 % V2O5 salt mixture at 700°C for 50 cycles. Each cycle consisting of 1 hour heating in a silicon carbide tubular furnace followed by 20 min of cooling. The thermogravimetric technique was used to determine the kinetics of corrosion. The scanning electron microscopy (SEM), energy dispersive analysis (EDAX), electron probe microanalyser (EPMA) and X-ray diffracton (XRD) techniques were used to evaluate the characterization of coatings with regard to coating bondstrength, thickness, microhardness and porosity. The parabolic rate constants of coated steels are lower when compared to the uncoated substrate. The NiCrAlY+ Cr2O3+YSZ coating is found to be more protective when compared to NiCrAlY+ TiO2 coating. The oxides of Al2O3, NiCr2O4, and Cr2O3 are formed on the outermost layer of the coatings which gives the resistance the coatings to high-temperature corrosion. © 2020en_US
dc.titleHot corrosion behavior of plasma-sprayed NiCrAlY/TiO2 and NiCrAlY/Cr2O3/YSZ cermets coatings on alloy steelen_US
dc.typeArticleen_US
Appears in Collections:1. Journal Articles

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.