Title: | Influence of Multi Axial Forging (MAF) on Microstructure and Mechanical Properties of Cu-Ti Alloy |
Authors: | Ramesh, S. Nayaka, H.S. Gopi, K.R. |
Issue Date: | 2018 |
Citation: | Materials Today: Proceedings, 2018, Vol.5, 11, pp.25534-25540 |
Abstract: | Multi axial forging (MAF) is one among the severe plastic deformation (SPD) processes, where large strains are imposed into the component. In the present work, as-received Cu-1.5%Ti alloy was subjected to MAF for 2 and 4 cycles at room temperature. Microstructure showed grain refinement after 2 and 4 cycles. Average grain size obtained for MAF processed samples after 2 and 4 cycles are 120 ?m and 40 ?m, respectively compared to initial grain size of 800 ?m. The Mechanical properties were analyzed for as-received and MAF processed samples. Tensile test showed increased ultimate tensile strength (493 MPa) for MAF 4-cycle sample compared to as-received (191 MPa) condition with accumulated strain of 2.18 for 4 cycles. Increase in hardness was observed for MAF processed sample of 143 Hv for 4-cycle compared to as-received sample of 67 Hv. � 2018 Elsevier Ltd. |
URI: | http://idr.nitk.ac.in/jspui/handle/123456789/8304 |
Appears in Collections: | 2. Conference Papers |
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.